Fluoroelastomer Molding EE30675R

75 durometer tan AFLAS fluoroelastomer compound.

 % Fluorine: 57%
 Cure System: Peroxide
 Color: Tan
 Compounded for: Transfer & compression molding.
 Form Slab, Strip or Calendered Sheet.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.

Conditions: MDR .5 ARC 6 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 1.73 Inch/lbs.
 Max torque: 7.86 Inch/lbs.
 Scorch Ts1: 0.50 Minutes.
 Cure Tc90: 1.99 Minutes.

 Conditions: Press cured 20 minutes @ 350º F (177º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 1550 PSI (10.7 MPa)
 100% Modulus (Per ASTM D-412): 1050 PSI ( 7.2 MPa)
 Ultimate Elongation (Per ASTM D-412): 200 %
 Shore A Hardness (Per ASTM D-2240): 73 Pts.
 Specific Gravity (Per ASTM D-297): 2.05 (H2O=1)
 Compression Set (Per ASTM D-395): 32.64 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Transfer

Durometer

75

Polymer Type

AFLAS

Color

Tan

Form

Slab, Strip, Calendered Sheet

Minimum TensIle Strength (PSI)

1550