Fluoroelastomer Molding EE94476H

75 durometer black Viton™ GLTS fluoroelastomer compound

 % Fluorine: 66%
 Cure System: Peroxide
 Color: Black
 Compounded for: Extrusion, Compression & Transfer molding
 Form: Slab, Strip, Calendered Sheet, or Extruded pre-form
 Storage: Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.

Conditions: MDR .5º ARC 3 minutes @ 370ºF (188ºC) Per ASTM D-6204
 Min torque: 2.88 Inch/lbs.
 Max torque: 29.76 Inch/lbs.
 Scorch Ts1: 0.31 Minutes
 Cure Tc90: 0.69 Minutes

 Conditions: Press cured 10 minutes @ 370ºF (188ºC) and Post cured for 16 hours @ 480ºF (250ºC).
 Tensile Strength (Per ASTM D-412): 2515 PSI (17.3MPa)
 100% Modulus (Per ASTM D-412): 1023 PSI (7.1MPa)
 Ultimate Elongation (Per ASTM D-412): 207 %
 Shore A Hardness (Per ASTM D-2240): 72 Pts.
 Specific Gravity (Per ASTM D-297): 1.78 (H2O=1)
 Compression Set (Per ASTM D-395): 4.66 % Conditions: 22 hrs@ 392ºF (200ºC)





Additional Information

Application

Compression, Transfer

Durometer

75

Polymer Type

Viton GLTS™

Color

Black

Form

Extruded Pre-Form, Slab, Strip, Calendered Sheet

Minimum TensIle Strength (PSI)

2515