Fluoroelastomer Molding EE96255BXO

55 durometer black Viton A fluoroelastomer compound

 % Fluorine: 66%
 Cure System: Bisphenol
 Color: Black
 Compounded for: Transfer, injection & compression molding for larger cross section parts.
 Form Slab, Strip, Calendered Sheetor Pre-form.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
 Cured Products Large Cross section cord & profiles
 Stocked Item Yes

Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 1.08 Inch/lbs.
 Max torque: 9.46 Inch/lbs.
 Scorch Ts1: 0.59 Minutes.
 Cure Tc90: 0.88 Minutes.

 Conditions: Press cured 6 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 1472 PSI (10.1 Mpa)
 100% Modulus (Per ASTM D-412): 247 PSI (1.7 Mpa)
 Ultimate Elongation (Per ASTM D-412): 329 %
 Shore A Hardness (Per ASTM D-2240): 57 Pts.
 Specific Gravity (Per ASTM D-297): 1.85 (H2O=1)
 Compression Set (Per ASTM D-395): 11.11 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Injection, Transfer

Durometer

55

Polymer Type

Viton A™

Color

Black

Form

Extruded Pre-Form, Slab, Strip, Calendered Sheet

Minimum TensIle Strength (PSI)

1472

Stock

Yes

Cured Products