Fluoroelastomer Molding EE96264B

65 durometer black Viton A fluoroelastomer compound

% Fluorine: 66%
 Cure System: Bisphenol
 Color: Black
 Compounded for: Transfer & compression molding.
 Form Slab, Strip or Calendered Sheet.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
 Cured Product Sheet

Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 0.60 Inch/lbs.
 Max torque: 12.50 Inch/lbs.
 Scorch Ts1: 1.00 Minutes.
 Cure Tc90: 2.75 Minutes.

 Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 1900 PSI (13.1 Mpa)
 100% Modulus (Per ASTM D-412): 490 PSI (3.4 Mpa)
 Ultimate Elongation (Per ASTM D-412): 285 %
 Shore A Hardness (Per ASTM D-2240): 67 Pts.
 Specific Gravity (Per ASTM D-297): 1.93 (H2O=1)
 Compression Set (Per ASTM D-395): 11.85 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Transfer

Durometer

65

Polymer Type

Viton A™

Color

Black

Form

Slab, Strip, Calendered Sheet

Minimum TensIle Strength (PSI)

1900