Fluoroelastomer Molding EE96270A

70 durometer black Viton A fluoroelastomer compound.

 % Fluorine: 66%
 Cure System: Bisphenol
 Color: Black
 Compounded for: Transfer, injection & compression molding.
 Form Slab, Strip or Calendered Sheet or Pre-form.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
 Cured product O-ring cord, tubing, profile, sheet.
 Stock Yes

Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 1.19 Inch/lbs.
 Max torque: 19.14 Inch/lbs.
 Scorch Ts1: 0.67 Minutes.
 Cure Tc90: 1.10 Minutes.

 Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 1951 PSI (13.5 Mpa)
 100% Modulus (Per ASTM D-412): 733 PSI (5.1 Mpa)
 Ultimate Elongation (Per ASTM D-412): 199 %
 Shore A Hardness (Per ASTM D-2240): 70 Pts.
 Specific Gravity (Per ASTM D-297): 1.80 (H2O=1)
 Compression Set (Per ASTM D-395): 9.49 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Injection, Transfer

Durometer

70

Polymer Type

Viton A™

Color

Black

Form

Extruded Pre-Form, Slab, Strip, Calendered Sheet

Minimum TensIle Strength (PSI)

1951

Stock

Yes