Fluoroelastomer Molding EE96275BXO

75 durometer black Viton A fluoroelastomer compound

 % Fluorine: 66%
 Cure System: Bisphenol
 Color: Black
 Compounded for: Injection, Compression, Transfer Molding & Extrusion. Designed for thick(>.750″) cross sections.
 Form Slab, Strip, Calendered Sheet, or Extruded pre-form
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
 Cured Products Large cross section O-ring cord and profiles.
 Stocked: Yes

Conditions: MDR .5º ARC 6 minutes @ 370ºF (188ºC) Per ASTM D-6204
 Min torque: 1.24 Inch/lbs.
 Max torque: 22.38 Inch/lbs.
 Scorch Ts1: 0.67 Minutes
 Cure Tc90: 1.13 Minutes

 Conditions: Press cured 10 minutes @ 370ºF (188ºC) and Post cured for 16 hours @ 480ºF (250ºC).
 Tensile Strength (Per ASTM D-412): 1700 PSI (11.7Mpa)
 100% Modulus (Per ASTM D-412): 850 PSI (5.9Mpa)
 Ultimate Elongation (Per ASTM D-412): 150 %
 Shore A Hardness (Per ASTM D-2240): 77 Pts.
 Specific Gravity (Per ASTM D-297): 1.84 (H2O=1)
 Compression Set (Per ASTM D-395): 10.4 % Conditions: 22 hrs@ 392ºF (200ºC)





Additional Information

Application

Compression, Injection, Transfer

Durometer

75

Polymer Type

Viton A™

Color

Black

Form

Extruded Pre-Form, Slab, Strip, Calendered Sheet

Minimum TensIle Strength (PSI)

1700

Stock

Yes

Cured Products