Fluoroelastomer Molding EE97359A

60 durometer black Viton B fluoroelastomer compound

 % Fluorine: 68%
 Cure System: Bisphenol
 Color: Black
 Compounded for: Transfer & compression molding.
 Form Slab, Strip or Calendered Sheet.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
 Cured Product Sheet
 Stock Yes

Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 1.31 Inch/lbs.
 Max torque: 12.09 Inch/lbs.
 Scorch Ts1: 0.92 Minutes.
 Cure Tc90: 1.48 Minutes.

 Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 2200 PSI ( 15.2 Mpa)
 100% Modulus (Per ASTM D-412): 300 PSI ( 2.0 Mpa)
 Ultimate Elongation (Per ASTM D-412): 345 %
 Shore A Hardness (Per ASTM D-2240): 61 Pts.
 Specific Gravity (Per ASTM D-297): 1.89 (H2O=1)
 Compression Set (Per ASTM D-395): 13.5 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Transfer

Durometer

60

Polymer Type

Viton B™

Color

Black

Form

Slab, Strip, Calendered Sheet

Minimum TensIle Strength (PSI)

2200

Stock

Yes

Reviews

There are no reviews yet.

Be the first to review “Fluoroelastomer Molding EE97359A”

Your email address will not be published. Required fields are marked *

Select Extrusion Type


Please leave this field empty.