Fluoroelastomer Molding EE98190H

90 durometer black Viton™ GFS fluoroelastomer compound.

 % Fluorine: 70%
 Cure System: Peroxide
 Color: Black
 Compounded for: Transfer & compression molding.
 Form Slab, Strip, Calendered Sheet or Pre-form.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
 Cured products O-ring cord, tubing, and profiles.

Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 2.85 Inch/lbs.
 Max torque: 3.55 Inch/lbs.
 Scorch Ts1: 0.30 Minutes.
 Cure Tc90: 1.00 Minutes.

 Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 3125 PSI (21.5 MPa)
 100% Modulus (Per ASTM D-412): 2130 PSI (14.7 MPa)
 Ultimate Elongation (Per ASTM D-412): 170 %
 Shore A Hardness (Per ASTM D-2240): 90 Pts.
 Specific Gravity (Per ASTM D-297): 1.89 (H2O=1)
 Compression Set (Per ASTM D-395): N/A % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Transfer

Durometer

90

Polymer Type

Viton GFS™

Color

Black

Form

Extruded Pre-Form, Slab, Strip, Calendered Sheet

Minimum TensIle Strength (PSI)

3125

Stock

Yes