Fluoroelastomer Molding EE98485H

85 durometer black Viton™ GFLTS fluoroelastomer compound

 % Fluorine: 70%
 Cure System: Peroxide
 Color: Black
 Compounded for: Transfer & compression molding.
 Form Slab, Strip or Calendered Sheet.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.

Conditions: MDR .5 ARC 3 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 3.14 Inch/lbs.
 Max torque: 37.98 Inch/lbs.
 Scorch Ts1: 0.26 Minutes.
 Cure Tc90: 0.74 Minutes.

 Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 2774 PSI (19.1 MPa)
 100% Modulus (Per ASTM D-412): 1648 PSI (11.4 MPa)
 Ultimate Elongation (Per ASTM D-412): 166 %
 Shore A Hardness (Per ASTM D-2240): 88 Pts.
 Specific Gravity (Per ASTM D-297): 1.87 (H2O=1)
 Compression Set (Per ASTM D-395): N/A % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Transfer

Durometer

85

Polymer Type

Viton GFLTS™

Color

Black

Form

Slab, Strip, Calendered Sheet

Minimum TensIle Strength (PSI)

2774

Stock

Yes