Fluoroelastomer Molding MPF-1750

75 durometer, black, improved chemical resistance Perfluoroelastomer compound

 % Fluorine: 72.5%
 Cure System: Peroxide
 Color: Black
 Compounded for: Transfer & compression molding.
 Form Slab, Extruded Preform.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.

Conditions: MDR .5 ARC 6 minutes @ 350º F (177º C) Per ASTM D-6204.
 Min torque: 2.25 Inch/lbs.
 Max torque: 17.56 Inch/lbs.
 Scorch Ts1: 0.58 Minutes.
 Cure Tc90: 2.32 Minutes.

 Conditions: Press cured 10 minutes @ 350º F (177º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 2420 PSI (16.7 Mpa)
 100% Modulus (Per ASTM D-412): 1420 PSI (9.8 Mpa)
 Ultimate Elongation (Per ASTM D-412): 157 %
 Shore A Hardness (Per ASTM D-2240): 75 Pts.
 Specific Gravity (Per ASTM D-297): 2.04 (H2O=1)
 Compression Set (Per ASTM D-395): 36.5 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Transfer

Durometer

75

Polymer Type

Color

Black

Form

Extruded Pre-Form, Slab

Minimum TensIle Strength (PSI)

2420

Stock

Yes

Cured Products