Fluoroelastomer Molding MPF-2750

75 durometer black improved temperature resistant Perfluoroelastomer compound.

 % Fluorine: 72.5%
 Cure System: Nitrile
 Color: Black
 Compounded for: Trnasfer & compression molding.
 Form Slab & extruded preform.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.

Conditions: MDR .5 ARC 12 minutes @ 380º F (193º C) Per ASTM D-6204.
 Min torque: 0.72 Inch/lbs.
 Max torque: 14.26 Inch/lbs.
 Scorch Ts1: 1.29 Minutes.
 Cure Tc90: 4.66 Minutes.

 Conditions: Press cured 7 minutes @ 380º F (193º C) and Post cured for 24 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 1495 PSI (10.3 Mpa)
 100% Modulus (Per ASTM D-412): 788 PSI ( 5.4 Mpa)
 Ultimate Elongation (Per ASTM D-412): 229 %
 Shore A Hardness (Per ASTM D-2240): 74 Pts.
 Specific Gravity (Per ASTM D-297): 2.01 (H2O=1)
 Compression Set (Per ASTM D-395): N/A % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Transfer

Durometer

75

Polymer Type

Color

Black

Form

Extruded Pre-Form, Slab

Minimum TensIle Strength (PSI)

1495

Stock

Yes

Cured Products