Fluoroelastomer Molding MPF-2900

90 durometer black improved temperature resistant Perfluoroelastomer compound

 % Fluorine: 57%
 Cure System: Nitrile
 Color: Black
 Compounded for: Compression molding.
 Form Slab & uncured preform.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.

Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 2.11 Inch/lbs.
 Max torque: 21.23 Inch/lbs.
 Scorch Ts1: 1.77 Minutes.
 Cure Tc90: 4.58 Minutes.

 Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 2285 PSI (15.8 Mpa)
 100% Modulus (Per ASTM D-412): N/A PSI ( N/A Mpa)
 Ultimate Elongation (Per ASTM D-412): 85 %
 Shore A Hardness (Per ASTM D-2240): 86 Pts.
 Specific Gravity (Per ASTM D-297): 1.99 (H2O=1)
 Compression Set (Per ASTM D-395): N/A % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression

Durometer

90

Polymer Type

Color

Black

Form

Slab

Minimum TensIle Strength (PSI)

2285

Stock

Yes

Cured Products