0.079″+/- .008_(2.01+/-.21 MM) 75 D_BRN_FKM_O-RING CORD
Fluoroelastomer Specialists
% Fluorine: | 66% |
Cure System: | Bisphenol |
Color: | Brown |
Compounded for: | Molding: (Compression, Injection, Transfer) |
Form: | Pre-Form, Slab, Strip or Calendered Sheet. |
Storage: | Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months. |
Stock: | Yes |
Typical Rheological Properties: Conditions: MDR .5 ARC 4 minutes @ 370° F (188° C) Per ASTM D-6204.
Min torque: | 1.30 Inch/lbs. |
Max torque: | 23.25 Inch/lbs. |
Scorch Ts1: | 0.65 Minutes |
Cure Tc90: | 1.10 Minutes |
Typical Physical Properties: Conditions: Press cured 10 minutes @ 370° F (188° C) and Post cured for 16 hours @ 480° F (250° C).
Tensile Strength (Per ASTM D-412): | 2250 PSI (15.5 MPa) |
100% Modulus (Per ASTM D-412): | 920 PSI (6.3 MPa) |
Ultimate Elongation (Per ASTM D-412): | 198% |
Shore A Hardness (Per ASTM D-2240): | 76 Pts. |
Specific Gravity (Per ASTM D-297): | 1.85 (H2O=1) |
Compression Set (Per ASTM D-395): | 8.56% Conditions: 22 hrs @ 392° F (200° C) |
0.079″+/- .008_(2.01+/-.21 MM) 75 D_BRN_FKM_O-RING CORD
Standard Increment | 500 |
---|---|
UOM | FT |
Color | Brown |
Temp High | 400º F ( 204º C) |
Temp. Min - Dynamic | 1.4°F (-17°C) |
Temp. Min - Static | -25.6°F(-32°C ) |
Durometer | 75 |
Diameter | 0.079″ (2.0MM) |
Polymer Type | 3M™ Dyneon™ Fluoroelastomers |