1.250″+/-.060(31.75+/-.1.53MM) 75 D_BRN_FKM_O-RING CORD
Fluoroelastomer Specialists
% Fluorine: | 66% |
Cure System: | Bisphenol |
Color: | Brown |
Compounded for: | Injection, Compression, Transfer Molding & Extrusion. Designed for thick(>.750″) cross sections. |
Form: | Slab, Strip, Calendered Sheet, or Extruded pre-form |
Storage: | Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months. |
Stocked: | Yes |
Typical Rheological Properties: Conditions: MDR .5º ARC 6 minutes @ 370ºF (188ºC) Per ASTM D-6204
Min torque: | 1.24 Inch/lbs. |
Max torque: | 22.38 Inch/lbs. |
Scorch Ts1: | 0.67 Minutes |
Cure Tc90: | 1.13 Minutes |
Typical Physical Properties: Conditions: Press cured 10 minutes @ 370ºF (188ºC) and Post cured for 16 hours @ 480ºF (250ºC).
Tensile Strength (Per ASTM D-412): | 1700 PSI (11.7Mpa) |
100% Modulus (Per ASTM D-412): | 850 PSI (5.9Mpa) |
Ultimate Elongation (Per ASTM D-412): | 150 % |
Shore A Hardness (Per ASTM D-2240): | 77 Pts. |
Specific Gravity (Per ASTM D-297): | 1.84 (H2O=1) |
Compression Set (Per ASTM D-395): | 10.4% Conditions: 22 hrs@ 392ºF (200ºC) |
1.250″+/-.060(31.75+/-.1.53MM) 75 D_BRN_FKM_O-RING CORD
Standard Increment | 25 |
---|---|
UOM | FT |
Color | Brown |
Temp High | 400º F ( 204º C) |
Temp. Min - Dynamic | 1.4°F (-17°C) |
Temp. Min - Static | -25.6°F(-32°C ) |
Durometer | 75 |
Diameter | 1.250″ (31.8MM) |
Polymer Type | 3M™ Dyneon™ Fluoroelastomers |