Additional Information
Application | Compression, Transfer |
---|---|
Durometer | 75 |
Polymer Type | – |
Color | Black |
Form | Extruded Pre-Form, Slab |
Minimum TensIle Strength (PSI) | 2535 |
Stock | Yes |
Cured Products | – |
75 durometer, black, improved chemical resistance Perfluoroelastomer compound
% Fluorine: 72.5%
Cure System: Peroxide
Color: Black
Compounded for: Transfer & compression molding.
Form Slab, Extruded Preform.
Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
Conditions: MDR .5 ARC 6 minutes @ 350º F (177º C) Per ASTM D-6204.
Min torque: 2.13 Inch/lbs.
Max torque: 15.15 Inch/lbs.
Scorch Ts1: 0.56 Minutes.
Cure Tc90: 1.98 Minutes.
Conditions: Press cured 10 minutes @ 350º F (177º C) and Post cured for 16 hours @ 480º F (250 ºC).
Tensile Strength (Per ASTM D-412): 2535 PSI (17.5 MPa)
100% Modulus (Per ASTM D-412): 1435 PSI (9.9 MPa)
Ultimate Elongation (Per ASTM D-412): 159 %
Shore A Hardness (Per ASTM D-2240): 75 Pts.
Specific Gravity (Per ASTM D-297): 2.04 (H2O=1)
Compression Set (Per ASTM D-395): 37.7 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)
Application | Compression, Transfer |
---|---|
Durometer | 75 |
Polymer Type | – |
Color | Black |
Form | Extruded Pre-Form, Slab |
Minimum TensIle Strength (PSI) | 2535 |
Stock | Yes |
Cured Products | – |