Viton Fluoroelastomer Compound EE77490H

90 durometer black Viton™ ETP fluoroelastomer compound.

Categories: , ,

 Type: Viton ETP
 % Fluorine: 67%
 Cure System: Peroxide
 Color: Black
 Compounded for: Transfer & compression molding.
 Form Slab, Strip, Calendered Sheet, or Pre-form.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
 Cured Products O-ring cord, tubing, profiles

Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 1.62 Inch/lbs.
 Max torque: 21.08 Inch/lbs.
 Scorch Ts1: 0.35 Minutes.
 Cure Tc90: 1.22 Minutes.

 Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 2954 PSI ( 20.4 MPa)
 100% Modulus (Per ASTM D-412): 2119 PSI (14.6 MPa)
 Ultimate Elongation (Per ASTM D-412): 154 %
 Shore A Hardness (Per ASTM D-2240): 90 Pts.
 Specific Gravity (Per ASTM D-297): 1.86 (H2O=1)
 Compression Set (Per ASTM D-395): 27.93 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Transfer
Durometer

90
Polymer Type

Viton ETP™
Color

Black
Form

Extruded Pre-Form, Slab, Strip, Calendered Sheet
Minimum TensIle Strength (PSI)

2954
Stock

Yes