Viton Fluoroelastomer Compound EE94490H

90 durometer black Viton™ GLTS fluoroelastomer compound.

Categories: , ,

 Type: Viton GLTS
 % Fluorine: 64%
 Cure System: Peroxide
 Color: Black
 Compounded for: Transfer & compression molding.
 Form Slab, Strip or Calendered Sheet.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.

Conditions: MDR .5 ARC 6 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 4.55 Inch/lbs.
 Max torque: 40.41 Inch/lbs.
 Scorch Ts1: 0.26 Minutes.
 Cure Tc90: 0.80 Minutes.

 Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 3414 PSI ( 23.5 MPa)
 100% Modulus (Per ASTM D-412): 2320 PSI ( 16.0 MPa)
 Ultimate Elongation (Per ASTM D-412): 138 %
 Shore A Hardness (Per ASTM D-2240): 91 Pts.
 Specific Gravity (Per ASTM D-297): 1.83 (H2O=1)
 Compression Set (Per ASTM D-395): 14.11 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Transfer
Durometer

90
Polymer Type

Viton GLTS™
Color

Black
Form

Slab, Strip, Calendered Sheet
Minimum TensIle Strength (PSI)

3414
Stock

Yes
Cured Products

–