Part #ee96255bxo

Viton Fluoroelastomer Compound EE96255BXO

55 durometer black Viton A fluoroelastomer compound

Durometer: 55
Color: Black
Polymer: Viton A™
% Fluorine: 66%
Cure System: Bisphenol
Color: Black
Compounded for: Transfer, injection & compression molding for larger cross section parts
Form: Slab, Strip, Calendered Sheetor Pre-form.
Storage: Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
Cured Products: Large Cross section cord & profiles
Stock: Yes

Typical Rheological Properties:
Conditions: MDR .5 ARC 4 minutes @ 370° F (188° C) Per ASTM D-6204.

Min torque: 1.08 Inch/lbs
Max torque: 9.46 Inch/lbs.
Scorch Ts1: 0.59 Minutes.
Cure Tc90: 0.88 Minutes.

Typical Physical Properties:
Conditions: Press cured 10 minutes @ 370° F (188° C) and Post cured for 16 hours @ 480° F (250° C).

Tensile Strength (Per ASTM D-412): 1472 PSI (10.1 Mpa)
100% Modulus (Per ASTM D-412): 247 PSI (1.7 Mpa)
Ultimate Elongation (Per ASTM D-412): 329 %
Shore A Hardness (Per ASTM D-2240): 57 Pts.
Specific Gravity (Per ASTM D-297): 1.85 (H2O=1)
Compression Set (Per ASTM D-395): 11.11 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)
To place an order, Minimum Quantity must be 1 ft.

Additional information

Application

Compression, Injection, Transfer

Durometer

55

Polymer Type

Viton A™

Color

Black

Form

Extruded Pre-Form, Slab, Strip, Calendered Sheet

Minimum TensIle Strength (PSI)

1472

Stock

Yes

Cured Products