90 durometer black Viton A fluoroelastomer
Type: Viton A
% Fluorine: 66%
Cure System: Bisphenol
Color: Black
Compounded for: Compression molding.
Form Slab, Strip or Calendered Sheet.
Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
Conditions: MDR .5 ARC 3 minutes @ 370º F (188º C) Per ASTM D-6204.
Min torque: 4.5 Inch/lbs.
Max torque: 35.28 Inch/lbs.
Scorch Ts1: 0.44 Minutes.
Cure Tc90: 0.91 Minutes.
Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
Tensile Strength (Per ASTM D-412): 2957 PSI (20.0 MPa)
100% Modulus (Per ASTM D-412): N/A PSI
Ultimate Elongation (Per ASTM D-412): 80 %
Shore A Hardness (Per ASTM D-2240): 91 Pts.
Specific Gravity (Per ASTM D-297): 2.12 (H2O=1)
Compression Set (Per ASTM D-395): 11.67 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)
Application | Compression |
---|---|
Durometer | 90 |
Polymer Type | Viton A™ |
Color | Black |
Form | Slab, Strip, Calendered Sheet |
Minimum TensIle Strength (PSI) | 2957 |
Stock | Yes |
Cured Products | – |
Reviews
There are no reviews yet.