Viton Fluoroelastomer Compound EE96292B

90 durometer black Viton A fluoroelastomer food grade compound

Categories: , ,

 Type: Viton A
 % Fluorine: 66%
 Cure System: Bisphenol
 Color: Black
 Compounded for: Extrusion, transfer & compression molding.
 Form Slab, Strip or Calendered Sheet.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
 Cured Product Sheet

Conditions: MDR .5 ARC 6 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 2.4 Inch/lbs.
 Max torque: 32.9 Inch/lbs.
 Scorch Ts1: 0.5 Minutes.
 Cure Tc90: 1.4 Minutes.

 Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 1775 PSI (12.2 Mpa)
 100% Modulus (Per ASTM D-412): 1275 PSI (8.8 Mpa)
 Ultimate Elongation (Per ASTM D-412): 130 %
 Shore A Hardness (Per ASTM D-2240): 90 Pts.
 Specific Gravity (Per ASTM D-297): 2.61 (H2O=1)
 Compression Set (Per ASTM D-395): 16.8 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)

Additional Information

Application

Compression, Transfer
Durometer

90
Polymer Type

Viton A™
Color

Black
Form

Slab, Strip, Calendered Sheet
Minimum TensIle Strength (PSI)

1775
Stock

No
Compounded to Meet

FDA Compliant