Additional information
Application | Compression, Transfer |
---|---|
Durometer | 90 |
Polymer Type | Viton B™ |
Color | Black |
Form | Slab, Strip, Calendered Sheet |
Minimum TensIle Strength (PSI) | 2050 |
Stock | Yes |
Cured Products | – |
90 durometer black Viton B fluoroelastomer compound
% Fluorine: | 68% |
Cure System: | Bisphenol |
Color: | Black |
Compounded for: | Transfer & compression molding |
Form: | Slab, Strip or Calendered Sheetand Pre-form |
Storage: | Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months. |
Typical Rheological Properties:
Conditions: MDR .5 ARC 4 minutes @ 370° F (188° C) Per ASTM D-6204.
Min torque: | 15.00 Inch/lbs. |
Max torque: | 60.00 Inch/lbs. |
Scorch Ts1: | 1.90 Minutes. |
Cure Tc90: | 6.75 Minutes. |
Typical Physical Properties:
Conditions: Press cured 10 minutes @ 370° F (188° C) and Post cured for 16 hours @ 480° F (250° C).
Tensile Strength (Per ASTM D-412): | 2050 PSI (14.1 Mpa) |
100% Modulus (Per ASTM D-412): | 1300 PSI (8.9 Mpa) |
Ultimate Elongation (Per ASTM D-412): | 180 % |
Shore A Hardness (Per ASTM D-2240): | 90 Pts. |
Specific Gravity (Per ASTM D-297): | 1.87 (H2O=1) |
Compression Set (Per ASTM D-395): | N/A % Conditions: 22 hrs@ 392ºF (200ºC) |
Application | Compression, Transfer |
---|---|
Durometer | 90 |
Polymer Type | Viton B™ |
Color | Black |
Form | Slab, Strip, Calendered Sheet |
Minimum TensIle Strength (PSI) | 2050 |
Stock | Yes |
Cured Products | – |
Send us a message and one of our customer service representatives will contact you within 24 hours.
Contact ×