Viton Fluoroelastomer Compound EE97362B

60 durometer black Viton B fluoroelastomer compound.

Categories: , ,

 Type: Viton B
 % Fluorine: 68%
 Cure System: Bisphenol
 Color: Black
 Compounded for: Transfer & compression molding.
 Form Slab, Strip or Calendered Sheet.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
 Stock Yes

Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 1.2 Inch/lbs.
 Max torque: 9.6 Inch/lbs.
 Scorch Ts1: .9 Minutes.
 Cure Tc90: 1.5 Minutes.

 Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 2200 PSI (15.2 Mpa)
 100% Modulus (Per ASTM D-412): 250 PSI (1.7 Mpa)
 Ultimate Elongation (Per ASTM D-412): 380 %
 Shore A Hardness (Per ASTM D-2240): 60 Pts.
 Specific Gravity (Per ASTM D-297): 1.89 (H2O=1)
 Compression Set (Per ASTM D-395): 18.12 % CONDITIONS: 22 hrs@ 392 ºF (200ºC)

Additional Information

Application

Compression, Transfer
Durometer

60
Polymer Type

Viton B™
Color

Black
Form

Slab, Strip, Calendered Sheet
Minimum TensIle Strength (PSI)

2200
Stock

Yes
Cured Products

–