Viton Fluoroelastomer Compound EE97370A

70 Durometer black Viton B fluoroelastomer compound

Durometer: 70
Color: Black
Polymer: Viton B™
% Fluorine: 68%
Cure System: Bisphenol
Color: Black
Compounded for: Transfer & compression molding
Form: Slab, Strip, Calendered Sheet.
Storage: Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.
Stock: No

Typical Rheological Properties:
Conditions: MDR .5 ARC 4 minutes @ 370° F (188° C) Per ASTM D-6204.

Min torque: 1.50 Inch/lbs.
Max torque: 14.25 Inch/lbs.
Scorch Ts1: 0.90 Minutes.
Cure Tc90: 2.05 Minutes.

Typical Physical Properties:
Conditions: Press cured 10 minutes @ 370° F (188° C) and Post cured for 16 hours @ 480° F (250° C).

Tensile Strength (Per ASTM D-412): 2250 PSI (15.5 Mpa)
100% Modulus (Per ASTM D-412): 410 PSI (2.8Mpa)
Ultimate Elongation (Per ASTM D-412): 335 %
Shore A Hardness (Per ASTM D-2240): 67 Pts.
Specific Gravity (Per ASTM D-297): 1.89 (H2O=1)
Compression Set (Per ASTM D-395): 17.74 % Conditions: 22 hrs@ 392ºF (200ºC)
To place an order, Minimum Quantity must be 1 ft.

Additional information

Application

Compression, Transfer

Durometer

70

Polymer Type

Viton B™

Color

Black

Form

Slab, Strip, Calendered Sheet

Minimum TensIle Strength (PSI)

2250