Viton Fluoroelastomer Compound EE98366M

65 durometer black Viton™ F fluoroelastomer compound for bonding to metal.

Categories: , ,

 Type: Viton F
 % Fluorine: 70%
 Cure System: Bisphenol
 Color: Black
 Compounded for: Transfer & compression molding.
 Form Slab, Strip or Calendered Sheet.
 Storage Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months.

Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
 Min torque: 1.25 Inch/lbs.
 Max torque: 15.50 Inch/lbs.
 Scorch Ts1: 0.80 Minutes.
 Cure Tc90: 1.90 Minutes.

 Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
 Tensile Strength (Per ASTM D-412): 2200 PSI (15.2 MPa)
 100% Modulus (Per ASTM D-412): 480 PSI (3.3MPa)
 Ultimate Elongation (Per ASTM D-412): 295 %
 Shore A Hardness (Per ASTM D-2240): 68 Pts.
 Specific Gravity (Per ASTM D-297): 1.96 (H2O=1)
 Compression Set (Per ASTM D-395): N/A % CONDITIONS: 22 hrs@ 392 ºF (200ºC)





Additional Information

Application

Compression, Transfer
Durometer

65
Polymer Type

Viton F™
Color

Black
Form

Slab, Strip, Calendered Sheet
Minimum TensIle Strength (PSI)

2200
Stock

Yes
Cured Products

–