| % Fluorine: | 66% |
| Cure System: | Bisphenol |
| Color: | Black |
| Compounded for: | Molding:(Compression, Injection, Transfer) |
| Form: | Pre-Form, Slab, Strip or Calendered Sheet |
| Storage: | Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months. |
| Cured Products: | O-Ring Cord, Profiles, Tubing |
| Stock: | Yes |
Typical Rheological Properties:
Conditions: MDR .5 ARC 4 minutes @ 370° F (188° C) Per ASTM D-6204.
| Min torque: | 0.91 Inch/lbs. |
| Max torque: | 12.78 Inch/lbs |
| Scorch Ts1: | 0.75 Minutes |
| Cure Tc90: | 1.08 Minutes. |
Typical Physical Properties:
Conditions: Press cured 10 minutes @ 370° F (188° C) and Post cured for 16 hours @ 480° F (250° C).
| Tensile Strength (Per ASTM D-412): | 1700 PSI (11.7 Mpa) |
| 100% Modulus (Per ASTM D-412): | 375 PSI ( 2.6 Mpa) |
| Ultimate Elongation (Per ASTM D-412): | 240 % |
| Shore A Hardness (Per ASTM D-2240): | 61 Pts |
| Specific Gravity (Per ASTM D-297): | 1.89 (H2O=1) |
| Compression Set (Per ASTM D-395): | 8.0 % CONDITIONS: 22 hrs@ 392 ºF (200ºC) |
| Application | Compression, Injection, Transfer |
|---|---|
| Durometer | 60 |
| Polymer Type | Viton A™ |
| Color | Black |
| Form | Extruded Pre-Form, Slab, Strip, Calendered Sheet |
| Minimum TensIle Strength (PSI) | 1700 |
| Stock | Yes |
| Compounded to Meet | – |