Additional information
Application | Compression, Injection, Transfer |
---|---|
Durometer | 75 |
Polymer Type | Viton A™ |
Color | Black |
Form | Extruded Pre-Form, Slab, Strip, Calendered Sheet |
Minimum TensIle Strength (PSI) | 2250 |
Stock | No |
Compounded to Meet | AMS 3216G |
% Fluorine: | 66% |
Cure System: | Bisphenol |
Color: | Black |
Compounded for: | Molding: (Compression, Injection, Transfer) |
Form: | Pre-Form, Slab, Strip or Calendered Sheet. |
Storage: | Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months. |
Cured Products: | O-Ring Cord, Profile, Sheet, Tubing |
Stock: | Yes |
Typical Rheological Properties:
Conditions: MDR .5 ARC 4 minutes @ 370° F (188° C) Per ASTM D-6204.
Min torque: | 1.30 Inch/lbs. |
Max torque: | 23.25 Inch/lbs. |
Scorch Ts1: | 0.65 Minutes. |
Cure Tc90: | 1.10 Minutes. |
Typical Physical Properties:
Conditions: Press cured 10 minutes @ 370° F (188° C) and Post cured for 16 hours @ 480° F (250° C).
Tensile Strength (Per ASTM D-412): | 2250 PSI (15.5 MPa) |
100% Modulus (Per ASTM D-412): | 920 PSI ( 6.3 MPa) |
Ultimate Elongation (Per ASTM D-412): | 198 % |
Shore A Hardness (Per ASTM D-2240): | 76 Pts |
Specific Gravity (Per ASTM D-297): | 1.85 (H2O=1) |
Compression Set (Per ASTM D-395): | 8.56 % CONDITIONS: 22 hrs@ 392 ºF (200ºC) |
Application | Compression, Injection, Transfer |
---|---|
Durometer | 75 |
Polymer Type | Viton A™ |
Color | Black |
Form | Extruded Pre-Form, Slab, Strip, Calendered Sheet |
Minimum TensIle Strength (PSI) | 2250 |
Stock | No |
Compounded to Meet | AMS 3216G |