Additional information
| Dimension | .062″+/-.016_X_36″_X_36″ (1.57+/-0.41MM_X_914.4+/-25.4MM) |
|---|---|
| Durometer | 75 |
| Color | Black |
| Polymer Type | Viton GLTS™ |
| Component Weight | 5.55 |
Fluoroelastomer Specialists
Part #SH5K4L0062
Viton Sheet SH5K4L0062
75 Durometer Black Viton GLTS™ Sheet – Compound EE94575H
Durometer: 75
Color: Black
Polymer: Viton GLTS™
Component Weight: 5.55
Color: Black
Polymer: Viton GLTS™
Component Weight: 5.55
| % Fluorine: | 64% |
| Cure System: | Peroxide |
| Color: | Black |
| Compounded for: | Molding:(Compression, Injection, Transfer) and Extrusion |
| Form: | Slab, Strip, Calendered Sheet, or Extruded pre-form |
| Storage: | Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months. |
| Cured Products: | O-Ring Cord, Profiles, Sheet, Tubing |
| Stock: | Yes |
Typical Rheological Properties: Conditions: MDR .5° ARC 3 minutes @ 370°F (188°C) Per ASTM D-6204.
| Min torque: | 2.34 Inch/lbs. |
| Max torque: | 28.67 Inch/lbs. |
| Scorch Ts1: | 0.35 Minutes |
| Cure Tc90: | 0.82 Minutes |
Typical Physical Properties: Conditions: Press cured 10 minutes @ 370°F (188°C) and Post cured for 16 hours @ 480°F (250°C).
| Tensile Strength (Per ASTM D-412): | 2200 PSI (15.2 MPa) |
| 100% Modulus (Per ASTM D-412): | 900 PSI (6.2 MPa) |
| Ultimate Elongation (Per ASTM D-412): | 220% |
| Shore A Hardness (Per ASTM D-2240): | 75 Pts. |
| Specific Gravity (Per ASTM D-297): | 1.78 (H2O=1) |
| Compression Set (Per ASTM D-395): | 7.4% Conditions: 22 hrs @ 392° F (200° C) |