Dimension | .188″+/-.031_X_36″_X_36″ (4.78+/-0.79MM_X_914.4+/-25.4MM) |
---|---|
Durometer | 80 |
Color | Black |
Polymer Type | Viton F™ |
Component Weight | 17.87 |
80 Durometer Black Viton F™ Sheet – Compound EE98380L
% Fluorine: | 70% |
Cure System: | Bisphenol |
Color: | Black |
Compounded for: | Transfer & compression molding. |
Form: | Pre-form, Slab, Strip or Calendered Sheet. |
Storage: | Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months. |
Cured Products: | O-Ring Cord, Profiles, Sheet, Tubing |
Stock: | Yes |
Typical Rheological Properties: Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
Min torque: | 1.40 Inch/lbs. |
Max torque: | 18.30 Inch/lbs. |
Scorch Ts1: | 0.65 Minutes |
Cure Tc90: | 1.15 Minutes |
Typical Physical Properties: Conditions: Press cured 5 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
Tensile Strength (Per ASTM D-412): | 2130 PSI (14.7 MPa) |
100% Modulus (Per ASTM D-412): | 900 PSI (6.2 MPa) |
Ultimate Elongation (Per ASTM D-412): | 215% |
Shore A Hardness (Per ASTM D-2240): | 79 Pts. |
Specific Gravity (Per ASTM D-297): | 1.89 (H2O=1) |
Compression Set (Per ASTM D-395): | 24.00% Conditions: 22 hrs @ 392° F (200° C) |
Dimension | .188″+/-.031_X_36″_X_36″ (4.78+/-0.79MM_X_914.4+/-25.4MM) |
---|---|
Durometer | 80 |
Color | Black |
Polymer Type | Viton F™ |
Component Weight | 17.87 |