Additional information
| Dimension | .375″+/-.047_X_36″_X_36″ (9.53+/-1.19MM_X_914.4+/-25.4MM) |
|---|---|
| Durometer | 80 |
| Color | Black |
| Polymer Type | Viton F™ |
| Component Weight | 33.66 |
Fluoroelastomer Specialists
Part #SHFTYPE/0375
Viton Sheet SHFTYPE/0375
80 Durometer Black Viton F™ Sheet – Compound EE98380L
Durometer: 80
Color: Black
Polymer: Viton F™
Component Weight: 33.66
Color: Black
Polymer: Viton F™
Component Weight: 33.66
| % Fluorine: | 70% |
| Cure System: | Bisphenol |
| Color: | Black |
| Compounded for: | Transfer & compression molding. |
| Form: | Pre-form, Slab, Strip or Calendered Sheet. |
| Storage: | Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months. |
| Cured Products: | O-Ring Cord, Profiles, Sheet, Tubing |
| Stock: | Yes |
Typical Rheological Properties: Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
| Min torque: | 1.40 Inch/lbs. |
| Max torque: | 18.30 Inch/lbs. |
| Scorch Ts1: | 0.65 Minutes |
| Cure Tc90: | 1.15 Minutes |
Typical Physical Properties: Conditions: Press cured 5 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
| Tensile Strength (Per ASTM D-412): | 2130 PSI (14.7 MPa) |
| 100% Modulus (Per ASTM D-412): | 900 PSI (6.2 MPa) |
| Ultimate Elongation (Per ASTM D-412): | 215% |
| Shore A Hardness (Per ASTM D-2240): | 79 Pts. |
| Specific Gravity (Per ASTM D-297): | 1.89 (H2O=1) |
| Compression Set (Per ASTM D-395): | 24.00% Conditions: 22 hrs @ 392° F (200° C) |