| % Fluorine: | 64% |
| Cure System: | Peroxide |
| Color: | Black |
| Compounded for: | Injection,Transfer, Compression Molding and Extrusion |
| Form: | Slab, Strip, Calendered Sheet, or Extruded pre-form |
| Storage: | Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months. |
Typical Rheological Properties: Conditions: MDR .5° ARC 3 minutes @ 370°F (188°C) Per ASTM D-6204.
| Min torque: | 2.10 Inch/lbs. |
| Max torque: | 24.29 Inch/lbs. |
| Scorch Ts1: | 0.30 Minutes |
| Cure Tc90: | 0.69 Minutes |
Typical Physical Properties: Conditions: Press cured 10 minutes @ 370°F (188°C) and Post cured for 16 hours @ 480°F (250°C).
| Tensile Strength (Per ASTM D-412): | 2700 PSI (18.6 MPa) |
| 100% Modulus (Per ASTM D-412): | 800 PSI (5.5 MPa) |
| Ultimate Elongation (Per ASTM D-412): | 250% |
| Shore A Hardness (Per ASTM D-2240): | 77 Pts. |
| Specific Gravity (Per ASTM D-297): | 1.84 (H2O=1) |
| Compression Set (Per ASTM D-395): | 20% Conditions: 22 hrs @ 392° F (200° C) |
| Application | Compression, Injection, Transfer |
|---|---|
| Durometer | 75 |
| Polymer Type | Viton GLT™ |
| Color | Black |
| Form | Extruded Pre-Form, Slab, Strip, Calendered Sheet |
| Minimum TensIle Strength (PSI) | 2250 |
| Stock | No |
| Compounded to Meet | AMS 3216G |
| Dimension | .180″+/-.015ID_X_.060″+/-.008W (4.57MM+/-0.39ID_1.52MM+/-0.21W) |
| Component Weight | 0.03 |