| % Fluorine: | 66% |
| Cure System: | Bisphenol |
| Color: | Black |
| Compounded for: | Molding: (Compression, Injection, Transfer) |
| Form: | Pre-Form, Slab, Strip or Calendered Sheet. |
| Storage: | Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months. |
| Cured Products: | O-Ring Cord, Profile, Sheet, Tubing |
| Stock: | Yes |
Typical Rheological Properties: Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
| Min torque: | 1.30 Inch/lbs. |
| Max torque: | 23.25 Inch/lbs. |
| Scorch Ts1: | 0.65 Minutes |
| Cure Tc90: | 1.10 Minutes |
Typical Physical Properties: Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
| Tensile Strength (Per ASTM D-412): | 2250 PSI (15.5 MPa) |
| 100% Modulus (Per ASTM D-412): | 920 PSI (6.3 MPa) |
| Ultimate Elongation (Per ASTM D-412): | 198% |
| Shore A Hardness (Per ASTM D-2240): | 76 Pts. |
| Specific Gravity (Per ASTM D-297): | 1.85 (H2O=1) |
| Compression Set (Per ASTM D-395): | 8.56% Conditions: 22 hrs @ 392° F (200° C) |
| Application | Compression, Injection, Transfer |
|---|---|
| Durometer | 75 |
| Polymer Type | Viton A™ |
| Color | Black |
| Form | Extruded Pre-Form, Slab, Strip, Calendered Sheet |
| Minimum TensIle Strength (PSI) | 2250 |
| Stock | No |
| Compounded to Meet | AMS 3216G |
| Dimension | .562″+/-.022ID_X_.062″+/-.010W (14.3MM+/-0.59ID_1.57MM+/-0.26W) |
| Component Weight | 0.1 |