| % Fluorine: | 68% |
| Cure System: | Bisphenol |
| Color: | Black |
| Compounded for: | Molding:(Compression, Injection, and Transfer) |
| Form: | Pre-Form, Slab, Strip or Calendered Sheet. |
| Storage: | Preserves best when stored in a cool/dry environment. Rheometer retesting suggested @ 6 months. |
| Cured Products: | O-Ring Cord, Profile, Sheet, Tubing |
| Stock: | Yes |
Typical Rheological Properties: Conditions: MDR .5 ARC 4 minutes @ 370º F (188º C) Per ASTM D-6204.
| Min torque: | 1.28 Inch/lbs. |
| Max torque: | 10.18 Inch/lbs. |
| Scorch Ts1: | 0.83 Minutes |
| Cure Tc90: | 1.37 Minutes |
Typical Physical Properties: Conditions: Press cured 10 minutes @ 370º F (188º C) and Post cured for 16 hours @ 480º F (250 ºC).
| Tensile Strength (Per ASTM D-412): | 2101 PSI (14.5 MPa) |
| 100% Modulus (Per ASTM D-412): | 244 PSI (1.7 MPa) |
| Ultimate Elongation (Per ASTM D-412): | 395% |
| Shore A Hardness (Per ASTM D-2240): | 60 Pts. |
| Specific Gravity (Per ASTM D-297): | 1.89 (H2O=1) |
| Compression Set (Per ASTM D-395): | 20.55% Conditions: 22 hrs @ 392° F (200° C) |
| Application | Compression, Injection, Transfer |
|---|---|
| Durometer | 60 |
| Polymer Type | FDA |
| Color | Black |
| Form | Extruded Pre-Form, Slab, Strip, Calendered Sheet |
| Minimum TensIle Strength (PSI) | 2250 |
| Stock | No |
| Compounded to Meet | AMS 3216G |
| Dimension | .157″+/-.010ID_X_.138″+/-.010W (3.99MM+/-0.26ID_3.51MM+/-0.26W) |
| Component Weight | 0.1 |